8000 Series Alloy Rods Aluminium AA8176 / 8030 alloy are a non-heat treatable wrought alloy. These are used in building wire and service cables. In some cases product from this Alloy is heat treated for making special service cable which have substantial elongation as well strength.
8000 Series Alloy Rods Aluminium AA8176 / 8030 alloy are a non-heat treatable wrought alloy. These are used in building wire and service cables. In some cases product from this Alloy is heat treated for making special service cable which have substantial elongation as well strength.
Aluminium AA8176 / 8030 alloy are a non-heat treatable wrought alloy. These are used in building wire and service cables. In some cases product from this Alloy is heat treated for making special service cable which have substantial elongation as well strength.
8000 Series Grades Al (min) Si (max) Fe Cu Cr Mg (Max) Diameter mm Tensile Strength Mpa (Min.) Elongation (%) Min. at 250 mm GL Conductivity (%) IACS Min 8176 Remainder 0.20 0.40 - 1.00 -- -- -- 9.5 110 8 60 8030 Remainder 0.10 0.30 – 0.80 0.15 – 0.30 -- 0.05 9.5 110 8 60.90
8000 Series Grades Al (min) Si (max) Fe Cu Cr Mg (Max) Diameter mm Tensile Strength Mpa (Min.) Elongation (%) Min. at 250 mm GL Conductivity (%) IACS Min 8176 Remainder 0.20 0.40 - 1.00 -- -- -- 9.5 110 8 60 8030 Remainder 0.10 0.30 – 0.80 0.15 – 0.30 -- 0.05 9.5 110 8 60.90
8000 Series Grades Al (min) Si (max) Fe Cu Cr Mg (Max) Diameter mm Tensile Strength Mpa (Min.) Elongation (%) Min. at 250 mm GL Conductivity (%) IACS Min 8176 Remainder 0.20 0.40 - 1.00 -- -- -- 9.5 110 8 60 8030 Remainder 0.10 0.30 – 0.80 0.15 – 0.30 -- 0.05 9.5 110 8 60.90